Alta Velocidad
Alta dureza, resistencia al desgaste y al calor.
| ACEROS PARA ALTA VELOCIDAD | |||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| UDDEHOLM | BOHLER | ANALISIS QUIMICO | Otros | Dureza de Suministro | AISI | DIN | |||||||||
| C | Si | Mn | Cr | Mo | W | V | Ni | Co | Al | ||||||
| S 600 | 0.85 | 4.2 | 5.1 | 6.3 | 2.0 | 240 | M2 | 1.3343 | |||||||
| S 500 | 1.10 | 3.9 | 9.2 | 1.4 | 1.2 | 8.0 | 280 | M-42 | 1.3247 | ||||||
| S 705 | 0.92 | 0.40 | 0.30 | 4.10 | 5.0 | 6.40 | 1.90 | 4.80 | 280 | M-35 | 1.3243 | ||||
| S 290 MICROCLEAN | 2.00 | 0.50 | 0.30 | 3.8 | 2.5 | 14.3 | 5.1 | 11.0 | 350 | ||||||
| S 390 MICROCLEAN | 1.64 | 0.60 | 0.30 | 4.8 | 2.0 | 10.4 | 4.8 | 8.0 | 300 | ||||||
| S 692 MICROCLEAN | 1.45 | 4 | 5.25 | 5.6 | 4 | S=0.03 | 280 | ||||||||
| S 790 MICROCLEAN | 1.3 | 4.2 | 5.0 | 6.3 | 3 | 280 | (M3:2) | 1.3345 | |||||||
| VANADIS 23 | 127 | 0.50 | 0.30 | 4.2 | 5.0 | 6.4 | 3.1 | 280 | (M3:2) | 1.3344 | |||||
| ACERO | RECOCIDO SUAVE | PRECALENTAMIENTO | TEMP. DE AUSTENITIZACIÓN | TEMPLE | DUREZA DESPUÉS DE REVENIDO | ||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| 100 | 200 | 300 | 400 | 500 | 550 | 600 | |||||
| ARNE | 280 | 870 | 800–850 | Aceite, aire | 64 | 63 | 61 | 59 | 57 | 56 | 55 |
| RIGOR | 280 | 860 | 800–850 | Aceite, aire | 65 | 64 | 62 | 61 | 60 | 59 | 58 |
| SVERKER 21 | 280 | 860 | 960–980 | Aceite, aire | 64 | 63 | 61 | 60 | 58 | 57 | 56 |
| K340 ISODUR | 280 | 860 | 1030–1050 | Aceite, aire | 64 | 63 | 61 | 60 | 58 | 57 | 55 |
| K360 ISODUR | 280 | 860 | 1040–1080 | Aceite, aire | 65 | 64 | 62 | 61 | 60 | 59 | 58 |
| CALMAX | 280 | 860 | 950–980 | Aceite, aire | 59 | 58 | 56 | 54 | 52 | 50 | 48 |
| CALDIE | 280 | 860 | 1020–1050 | Aceite, aire | 60 | 59 | 58 | 56 | 54 | 53 | 50 |
| VANADIS 4 EXTRA | 280 | 860 | 1040–1080 | Aceite, aire | 65 | 64 | 63 | 61 | 60 | 58 | 56 |
| K294 | 280 | 860 | 1020–1040 | Aceite, aire | 65 | 64 | 63 | 61 | 59 | 58 | 56 |
| K390 Microclean | 280 | 860 | 1050–1100 | Aceite, aire | 66 | 65 | 64 | 63 | 61 | 59 | 57 |
| K490 Microclean | 280 | 860 | 1050–1100 | Aceite, aire | 65 | 64 | 63 | 61 | 59 | 57 | 55 |
| K890 Microclean | 280 | 860 | 1050–1100 | Aceite, aire | 66 | 65 | 64 | 62 | 60 | 58 | 56 |
| CARACTERÍSTICAS | ||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| ACERO RAPIDO PARA TRABAJO EN FRIO Y HERRAMIENTA DE CORTE CON BUENA RESISTENCIA AL DEGASTE | ACERO RAPIDO PARA CORTADORES PARA FRESAR, BROCAS, BURILES, BROCHAS Y HERRAMIENTAS DE CORTE DE ALTA PRODRUCCION | ACERO RAPIDO PARA CORTADORES PARA FRESAR, BROCAS, BURILES, BROCHAS Y HERRAMIENTAS DE CORTE DE ALTA PRODUCCION | ACERO RAPIDO DE METALURGIA DE POLVOS, DONDE ES REQUERIDA DURESAS DE 67-70 HRC EN HERRAMIENTAS DE CORTE. SINQUE PIERDA SU MAXIMA DUREZA Y TENACIDAD | METALURGIA DE POLVOS, PARA HERRAMIENTAS DE CORTE DE METALES NO FERROSOS Y TROQUELADOS DE PRECISION | METALURGIA DE POLVOS, PARA HERRAMIENTAS DE CORTE Y DADOS PEQUEÑOS DE FUNCION A PRESION | METALURGIA DE POLVOS PARA HERRAMIENTAS DE CORTE, CON LA TEGNOLOGIA 3G DE LA METALURGIA DE POLVOS QUE OFRECEN UNA EXCELENTE AL DESGASTE Y TENACIDAD CONTENIDO DE AZUFREM, EXELENTE PARA APLICACIONES EN FRIO | METALURGIA DE POLVOS PARA HERRAMIENTAS DE CORTE, EL PROCESO DE METALURGIA DE PLOVOS CARACTERISAZADO POR UNA ALTA RESISTENCIA AL DESGASTE, RESISTENCIA A LA COMPRECION Y TENACIDAD, TAMBIEN PARA APLICACIONES EN FRIO | |||||